T98 – NOVOLAC EPOXY CHEMICAL MORTAR

T98 – NOVOLAC EPOXY CHEMICAL MORTAR

Data Sheet

100% solids epoxy compound, Novolac epoxy filled with quartz, designed for concrete repair exposed to industrial environments with aggressive chemicals. Easily applied with trowel and spatula.

Application Areas

Coverage

Color

Packaging

Technical Data

Maximum Temperature (Dependent on service) Wet Service | Dry Service 65°C | 85°C 149°F | 185°F
Solids by Volume 100%
Thermal Compatibility with Concrete (ASTM C 884) Pass
Pot Life 45 min / kg at 72ºF
SAG Vertical Resistance at 21ºC (70ºF) 6mm (240mils) No sagging
Mixing Ratio – Liquid 3:1 by weight – Base: Activator
Mixing Ratio – Mortar 1:5 by weight – Resin Mix: Quartz
Shelf life (unopened containers) 3 Years at 55-95ºF (13-35ºC)

Application Sheet

Surface Preparation
Proper surface preparation is vital for long-term performance. The prepared concrete surface must be structurally sound, free of all contaminants, and roughened to a profile >ICRI CSP 3 (similar to #60 grit sandpaper). Taurus T98 can be applied directly onto concrete.

Mixing
To facilitate mixing and application, all material temperatures should be between 21°–32°C (70°–90°F) prior to mixing. Taurus T98 should be applied shortly after the application of T497 primer. The primer must remain tacky before applying T98; otherwise, the area must be re-primed. This is optimal within 2 hours of application, depending on environmental conditions. Pre-mix the Base to disperse pigments. Then thoroughly mix Base and Hardener in an appropriate container using a slow-speed mixer. After that, transfer the mixed resins into an epoxy mortar mixer containing one bag of quartz and add gradually. Total mixing time should be a minimum of 3 minutes or until uniformly blended.

Application
Mixed Taurus T98 can be distributed over the floor surface using screed bars, screed boxes, or similar tools, not exceeding 1.2 m (3.93 ft) in width. Apply a minimum of 6 mm (240 mils) and finish the surface with a steel trowel. IMPORTANT: During application, firmly press T98 onto the substrate to promote contact with the primer and ensure full compaction. Finish the mortar surface to a smooth, closed surface texture.

Cured Time:

16°C (60°F) 25°C (77°F) 32°C (90°F)
Tack Free 4 hours 2 hours 1 hour
Light Load 12 hours 6 hours 3 hours
Overcoat End 16 hours 10 hours 5 hours
Full Load 24 hours 12 hours 6 hours
Full Chemical 48 hours 24 hours 12 hours

Clean: Tools should be thoroughly cleaned immediately after use with a strong alkaline detergent.

Safety: Before using any product, review the Safety Data Sheet (SDS) or Safety Data Sheet for your area. Follow standard confined space
entry and work procedures, if applicable.

Download Product Data Sheet PDF


Download Safety Data Sheet PDF


The manufacturer, Taurus Epoxy Inc., makes no express or implied warranties, including warranties of merchantability or fitness for a particular purpose for this product. Under no circumstances shall the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability or any other theory arising from the use of this product. The information and recommendations contained herein are based on the Standard Product and are owned and provided solely for the use of our customers. This information is provided in good faith and is believed to be true and accurate as of the date/version of this document. As the manufacturer has no control over the conditions of use or the application process of the parts using this product, the manufacturer cannot accept responsibility for loss, injury or other damage resulting from the use of the Product or this or any other information provided by the manufacturer. Therefore, no warranties of any kind, express or implied, are made by the manufacturer, Taurus Epoxy Inc., with respect to this, or any, product manufactured by them or any contracted or licensed manufacturer. Taurus Epoxy products do not provide structural integrity or improvements. They are only used to provide protection against corrosion, wear, abrasion and chemical attack on a given substrate and only to the extent provided for in data sheets, data sheets, safety data sheets and any other information provided in writing directly from manufacturers’ technical support.