Brushable compound, 100% solid, with filling of ceramic micro spheres for protection from abrasion. Excellent chemical resistance with presence of caustics and acids. It is easily applied with brush, roller and airless.
| Maximum Temperature (Dependent on service) | Wet Service | Dry Service | 90°C | 150°C | 194°F | 320°F |
|---|---|---|---|
| Flexural Strength | (ASTM D 790) | 560 kg/cm2 (54.2 MPa) | 8,000 psi |
| Pull-Off Adhesion | (ASTM D 4541) | 330 kg/cm2 (32.4 MPa) | 4,700 psi |
| Tensile Strength | (ASTM D 638) | 240 kg/cm2 (23.4 MPa) | 3,400 psi |
| Hardness of the Shore D Durometer | (ASTM D 2240) | 85 | |
| Working time | 25 min / kg at 72ºF | ||
| SAG Vertical Resistance at 21ºC (70ºF) and 0.6mm (240mils) | No sagging | ||
| Mix Ratio | 2:1 by Weight | Base: Activator | |
| Shelf life (unopened containers) | 3 Years at 55-95ºF (13-35ºC) | ||
Surface Preparation
Proper surface preparation is critical to the long-term performance of this product. The exact requirements for surface preparation vary with the severity of the application, expected service life, and the initial substrate conditions. All sharp edges and welds shall be ground smooth or to a 3 mm (120 mil) radius before abrasive blasting. Optimum preparation will provide a surface thoroughly cleaned of all contaminants and roughened to an angular profile between 75-125 μm (3-5 mil). This is normally achieved by initial cleaning and degreasing and then abrasive blasting to a cleanliness of White Metal (SSPC-SP10) or Near White Metal, followed by removal of residual abrasive blast residues from the surface to be coated.
Mixing
Mix the activator well in the base with the mixing rod scraping the sides and the bottom of the container. Mix by weight 2 parts Base to 1 part of Activator. Mix thoroughly to produce a uniform and without stripes. Never put solvents.
Application
Brush: medium to rigid bristles of sufficient quality than bristles do not come loose and stick to the coating (brushes of sows glued by epoxy are better).
Trim or put tape <1″nap.
Roller: use a good quality 1/8″nap.
Application Temperature: Keep between 55 to 95ºF (17 to 35ºC). Substrate: keep between 45 to 105ºF (7 to 40ºC). the difference in temperature of the substrate and the material should never exceed 10ºF, 5ºC. Substrate shall be a minimum of 5ºF (3ºC) above dew point. Do not apply if relative humidity exceeds 90%. If necessary, heat the metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight (75ºF+) for ease of mixing.
Cured Time:
| 16°C (60°F) | 25°C (77°F) | 32°C (90°F) | |
|---|---|---|---|
| Tack Free | 3 hours | 1.5 hours | 1 hour |
| Light Load | 6 hours | 3 hours | 2 hours |
| Term Overlay | 8 hours | 5 hours | 3 hours |
| Full Charge | 10 hours | 6 hours | 4 hours |
| Complete Chemical | 12 hours | 8 hours | 6 hours |
Clean: Tools should be thoroughly cleaned immediately after use with a strong alkaline detergent.
Safety: Before using any product, review the Safety Data Sheet (SDS) or Safety Data Sheet for your area. Follow standard confined space
entry and work procedures, if applicable.
FDA Complicance: This product complies with FDA regulations: FDA 21 CFR 175.300 and FDA 21 CFR 175.105.
The manufacturer, Taurus Epoxy Inc., makes no express or implied warranties, including warranties of merchantability or fitness for a particular purpose for this product. Under no circumstances shall the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability or any other theory arising from the use of this product. The information and recommendations contained herein are based on the Standard Product and are owned and provided solely for the use of our customers. This information is provided in good faith and is believed to be true and accurate as of the date/version of this document. As the manufacturer has no control over the conditions of use or the application process of the parts using this product, the manufacturer cannot accept responsibility for loss, injury or other damage resulting from the use of the Product or this or any other information provided by the manufacturer. Therefore, no warranties of any kind, express or implied, are made by the manufacturer, Taurus Epoxy Inc., with respect to this, or any, product manufactured by them or any contracted or licensed manufacturer. Taurus Epoxy products do not provide structural integrity or improvements. They are only used to provide protection against corrosion, wear, abrasion and chemical attack on a given substrate and only to the extent provided for in data sheets, data sheets, safety data sheets and any other information provided in writing directly from manufacturers’ technical support.